Ceramic material

ABSTRACT

A material composed of a large fraction of aluminum oxide, zirconium oxide and strontium aluminate.

The invention relates to a ceramic material which is particularly suitable for dynamic stresses.

Ceramic materials offer a wide range of possible applications. Their composition can be adapted to their intended use by the targeted addition of specific elements and/or compounds thereof. Aluminium oxide and zirconium oxide, for example, are ceramic materials which, individually or in combination with one another, can be processed into cutting tools, catalyst supports or prostheses.

Ceramic materials are brittle and therefore not generally suitable for dynamic stresses, in particular caused by vibrations and impacts.

The object of the invention is to provide a ceramic material which is suitable for dynamic stresses.

Surprisingly, it has been shown that an aluminium oxide material of the composition listed in the following table in a sintered compact is suitable as a material having the ability to absorb energy under dynamic stress. This material is therefore particularly suitable for use as an armour ceramic, i.e. for the production of components in which energy absorption is necessary, such as e.g. in armour platings and particularly in body armour.

Material wt. % wt. % ZrO₂ 18 28 Cr₂O₃ 0 1 Y₂O₃ (relative to ZrO₂) 0 6 SrO 0 2 TiO₂ 0 0.5 MgO 0 0.5

Aluminium oxide to make up to 100 wt. %

The dominant structural component of a material combination of this type is aluminium oxide. The property-determining features, such as hardness, modulus of elasticity and thermal conductivity, are therefore very close to the properties of pure aluminium oxide. The components zirconium oxide and strontium aluminate are embedded in the aluminium oxide matrix. The raw materials are preferably used in high purity. As a result of the high purity of the raw materials, grain-boundary phases are only formed to an extremely small extent. The strontium aluminate forms characteristic plate-like crystallites, platelets, which make a significant contribution to the increase in strength.

The components zirconium oxide and strontium aluminate contribute to the increase in fracture toughness, which is about 60% higher than is the case with pure aluminium oxide. These reinforcing components result in an increase in strength by a factor of almost 2, and at the same time the damage tolerance, i.e. the property of the component to retain high residual strength even with possible damage, also increases.

When a sintered compact made of the material is under high mechanical stress, mechanisms are surprisingly activated which, for example, inhibit or stop crack propagation. The most important mechanism here is the stress-induced conversion of the zirconium oxide from the tetragonal to the monoclinic phase. The volume expansion of the zirconium oxide associated with the conversion causes the formation of local compressive stresses, which counteracts the external tensile load and thus prevents crack growth.

Surprisingly, the crack path is deflected by the embedded platelets, and so additional energy is absorbed during crack propagation.

It may be regarded as a special feature of the material according to the invention that the two mechanisms mutually reinforce one another so that the effective increase in fracture toughness is even greater than would be expected from the simple addition of the individual mechanisms.

A preferred material composition is listed below with its properties:

ED 4-point Min. break Weibull Batch, ZrO₂ Y₂O₃ Cr₂O₃ SrO 2000 strength strength modulus HV10 mono K_(lc) Grain size PL specs wt. % wt. % wt. % wt. % g/cm³ MPa MPa — — % MPa m^(0.5) μm min 24.0 0.50 0.26 0.70 4.360 1000 700 7 1740 10 5.5 medium max 25.5 0.65 0.35 0.85 ≧ ≧ ≧ ≧ ≦ ≧ 0.58

The Al₂O₃ content of 72.65 wt. % to 74.54 wt. % makes up the balance. Impurities due to the raw materials (<0.05 wt. %) are possible, but are not listed separately owing to their small proportion.

The production of sintered mouldings from the material according to the invention takes place by conventional ceramics technology. The essential process steps are:

-   -   a) Adding the powder mixture to water in the specified         composition, using liquifiers to avoid sedimentation.     -   b) Homogenising in a high-speed mixer.     -   c) Grinding in an attrition mill, thus increasing the specific         surface area of the powder mixture (=comminution).     -   d) Adding organic binders.     -   e) Spray-drying, resulting in free-flowing granules with defined         properties.     -   f) Moistening the granules with water.     -   g) Pressing axially or isostatically.     -   h) Green machining, largely forming the final contours taking         into account the shrinkage on sintering.     -   i) Pre-firing, during which shrinkage to approx. 98% of the         theoretical density occurs. Any remaining residual pores are         closed to the outside.     -   j) Hot isostatic pressing at high temperature and under high gas         pressure, resulting in almost complete final compression.     -   k) So-called white firing, resulting in equalisation of the         imbalance of the oxygen ions in the ceramic produced during hot         isostatic pressing.     -   l) Hard machining by grinding and polishing.     -   m) Annealing.

The properties of the sintered moulding made of the material according to the invention can be further reinforced by means of inclusions. Thus, it is possible to mix whiskers and/or fibres into the material before shaping a sintered compact, or to incorporate net-like structures or woven fabrics into the material in the green state. The whiskers, fibres or nets or woven fabrics must be made of a material which does not interact with the ceramic material in a way that would lead to an impairment of its properties. Furthermore, the material must not become modified during sintering in a way that would damage the material.

Sintered mouldings produced from the material according to the invention surprisingly combine the best properties of each of the intrinsically competing ceramic materials aluminium oxide and zirconium oxide, particularly for use as an armour ceramic: hardness, ageing resistance, wetting behaviour with respect to water and high thermal conductivity are properties known from sintered mouldings of aluminium oxide, and high strength and high fracture toughness, i.e. damage tolerance, are properties known from sintered mouldings of zirconium oxide. 

1-14. (canceled)
 15. A ceramic material comprising 72 to 82 wt. % Al₂O₃, 18 to 28 wt. % ZrO₂, 0 to 1 wt. % Cr₂O₃, 0 to 6 wt. % Y₂O₃, 0 to 2 wt. % SrO, 0 to 0.5 wt. % TiO₂ and 0 to 0.5 wt. % MgO.
 16. A ceramic material according to claim 15, comprising 24.0 to 25.5 wt. % ZrO₂, 0.26 to 035 wt. % Cr₂O₃, 0.50 to 0.6 wt. % Y₂O₃, 0.70 to 0.85 wt. % SrO and Al₂O₃ to make up to 100 wt. %.
 17. A ceramic material according to claim 16, wherein the 4-point flexural strength is ≧1000 MPa.
 18. A ceramic material according to claim 16, wherein the fracture toughness K_(lc) is ≧5.5 MPam^(0.5).
 19. A ceramic material according to claim 16, wherein the Weibull modulus is ≧7.
 20. A ceramic material according to claim 16, wherein the hardness HV10 is ≧1740.
 21. A ceramic material according to claim 16, wherein the density ED2000 is ≧4.360 g/cm³.
 22. A ceramic material according to claim 15, wherein the material is additionally interspersed with whiskers or fibers or net-like structures or woven fabrics made of suitable materials.
 23. A ceramic material according to claim 15, wherein the components zirconium oxide and strontium aluminate are embedded in the aluminium-oxide matrix.
 24. A ceramic material according to claim 15, wherein the strontium aluminate is present in the form of plate-like crystallites, platelets.
 25. A sintered molding prepared by molding the ceramic material of claim 15 and sintering the molded ceramic material to form the sintered molding.
 26. The sintered ceramic material of claim
 15. 27. A component which absorbs energy under dynamic stress comprising the sintered material of claim
 15. 28. Armour platings containing the sintered ceramic material of claim
 15. 